Alcohol- and water-based flux EO-Y-006B (multiflux)

Recommended method of application
Wave and selective soldering

No Clean-Flux, alcohol-based, partially aqueous
Di-carboxylic acids, low VOC, halogen-free activated, with synthetic resin, rosin-free (WEEE/RoHS compliant)
Type ISO-9454: 2231 (2.2.3.A) DIN EN 61190-1-1 (IEC ORL0)

Cat.-No. 6065
6065-Kanister-30l-EO-Y-006B-EN_520x520px

Technical Data

Appearance: colourless, transparent liquid
Hazardous goods: Yes
VOC: 60 %
Solids content: 3.0 wt.-%
Acid number: 24 – 27 mg KOH/g
Halogen-free: Yes
Resiny: Yes
Density at 20 °C: 0.86 – 0.88 g/ml
Activators: di-carboxylic acids, synthetic resin
Solvents: alcohol- / partial water-based
Flash point: 20 °C
Available as concentrate: No
Durability: 12 months

Description

EO-Y-006B is universally suitable for the wave and selective soldering of circuit boards and contains organic, halogen-free, activating additives formulated with a small amount of synthetic resin. This flux was developed in a combination with leaded and lead-free solders, coordinated especially to the thermal requirements of the soldering process.
EO-Y-006B contains special alcoholic additives for the stabilization and improvement of the drying time in comparison with conventional water- or partially water-based fluxes.

Recommendations for the processing of this flux:
This flux is very versatile in use and OSP-compatible. Good results are achieved with manual, wave and selective soldering as well as for cable manufacture/strand tinning. The generally applicable rule, to basically select as little of the applied flux as possible, is also valid for this product.
Foam fluxes: Not recommended
Spray fluxes: With the possibility of dosing the amount of fluxing agent, first set to 30 – 40 ml/min., observe the even distribution of flux on the circuit board (if necessary test with heat-sensitive paper) and then adjust to the optimal amount.
 Pre-heating: With “simple” circuit boards a pre-heating temperature of 80 – 110 °C is recommended on the top side of the circuit board, with “more complex” boards a temperature of 100 – 130 °C is recommended. The operation can be carried out both in solder systems containing leaded as well as lead-free solder systems.

Customer added value

  • Wide range of applications (multiflux)
  • Very good soldering properties (capillarity, wetting)
  • Broad process window (high thermal stability, good activity over a long interval)
  • Very good residue behaviour (optically very clean, high SIR)

Packaging units

Canister: 5 l, 20 l
Other packaging units on request